Our company owns the magnesium production line
The raw material (dolomite) which is the qualified material crushed by the crusher is calcined into white by rotary kiln, cooled by the cooling machine and then mixed evenly with silicon powder (75%) and silica powder (including GaF2 fluorite=95%)
Being grinded into powder by ball mill, the marble machine will shape it as a ball which will be put into the reducing furnace after being equipped with the heat-resistant and stainless steel reduction jar
Then crude magnesium is restored and formed under the temperature of 1,200 to 1,250 degree Celsius and vacuum of -1.33Pa
By solvent refining, ingot casting and superficial treatment, the magnesium ingot is formed
Specifications (mm) |
Kiln demensions | Output(t/h) | Rotation speed(r/min) | Moto power(kw) | Weight | Note | ||
Diameter (mm) |
Length (mm) |
Obliquity (%) |
(t) | |||||
Ø1.4*33 | 1.4 | 33 | 3 | 0.9-1.3 | 0.39-3.96 | 18.5 | 47.5 | ---- |
Ø1.6*36 | 1.6 | 36 | 4 | 1.2-1.9 | 0.26-2.63 | 22 | 52 | ---- |
Ø1.8*45 | 1.8 | 45 | 4 | 1.9-2.4 | 0.16-1.62 | 30 | 78.2 | ---- |
Ø1.9*39 | 1.9 | 39 | 4 | 1.65-3 | 0.29-2.93 | 30 | 77.59 | ---- |
Ø2.0*40 | 2 | 40 | 3 | 2.5-4 | 0.23-2.26 | 37 | 119.1 | ---- |
Ø2.2*45 | 2.2 | 45 | 3.5 | 3.4-5.4 | 0.21-2.44 | 45 | 128.3 | ---- |
Ø2.5*40 | 2.5 | 40 | 3.5 | 9.0-10.5 | 0.44-2.44 | 55 | 149.61 | ---- |
Ø2.5*50 | 2.5 | 50 | 3 | 6.25-7.4 | 0.62-1.86 | 55 | 187.37 | ---- |
Ø2.5*54 | 2.5 | 54 | 3.5 | 6.9-8.5 | 0.48-1.45 | 55 | 196.29 | ---- |
Ø2.7*42 | 2.7 | 42 | 3.5 | 10.0-11.0 | 0.10-1.52 | 55 | 198.5 | ---- |
Ø2.8*44 | 2.8 | 44 | 3.5 | 12.5-13.5 | 0.437-2.18 | 55 | 201.58 | Suspension preheating kiln |
Ø3.0*45 | 3 | 45 | 3.5 | 12.8-14.5 | 0.5-2.47 | 75 | 210.94 | ---- |
Ø3.0*48 | 3 | 48 | 3.5 | 25.6-29.3 | 0.6-3.48 | 100 | 237 | Outside disassemble kiln |
Ø3.0*60 | 3 | 60 | 3.5 | 12.3-14.1 | 0.3-2 | 100 | 310 | ---- |
Ø3.2*50 | 3.2 | 50 | 4 | 40.5-42 | 0.6-3 | 125 | 278 | Outside disassemble kiln |